Effects of Lithium Source and Content on the Properties of Li-Rich Layered Oxide Cathode Materials (2023)


Wang, Y., Hietaniemi, M., Välikangas, J., Hu, T., Tynjälä, P., & Lassi, U. (2023). Effects of Lithium Source and Content on the Properties of Li-Rich Layered Oxide Cathode Materials. ChemEngineering, 7(1), Article 15. https://doi.org/10.3390/chemengineering7010015


JYU-tekijät tai -toimittajat


Julkaisun tiedot

Julkaisun kaikki tekijät tai toimittajatWang, Yufan; Hietaniemi, Marianna; Välikangas, Juho; Hu, Tao; Tynjälä, Pekka; Lassi, Ulla

Lehti tai sarjaChemEngineering

eISSN2305-7084

Julkaisuvuosi2023

Ilmestymispäivä14.02.2023

Volyymi7

Lehden numero1

Artikkelinumero15

KustantajaMDPI

JulkaisumaaSveitsi

Julkaisun kielienglanti

DOIhttps://doi.org/10.3390/chemengineering7010015

Julkaisun avoin saatavuusAvoimesti saatavilla

Julkaisukanavan avoin saatavuusKokonaan avoin julkaisukanava

Julkaisu on rinnakkaistallennettu (JYX)https://jyx.jyu.fi/handle/123456789/85689


Tiivistelmä

Lithium-rich layered oxide (LLO) are considered high-capacity cathode materials for next-generation lithium-ion batteries. In this study, LLO cathode materials were synthesized via the hydroxide coprecipitation method followed by a two-step lithiation process using different lithium contents and lithium sources. The effects of lithium content and lithium source on structure and electrochemical performance were investigated. This study demonstrated the clear impact of Li/TM ratio on electrochemical performance. Lower Li/TM ratio reduced the irreversible capacity loss in the first cycle and provided better cycling stability among all samples. The best results exhibited an initial discharge capacity of 279.65 mAh g−1 and reached a discharge capacity of 231.9 mAh g−1 (82.9% capacity retention) after 30 cycles. The sample using Li2CO3 as lithium source exhibits better electrochemical performance than the sample using LiOH as lithium source. Therefore, it is important to choose the appropriate lithium source and optimal lithium content for improving structural properties and electrochemical performance of LLO.


YSO-asiasanatlitiumioniakutelektroditmateriaalitlitiumoksiditsähkökemia

Vapaat asiasanatlithium-ion battery; cathode material; lithium-rich layered oxides; coprecipitation; lithium content; lithium source


Liittyvät organisaatiot


OKM-raportointiKyllä

Raportointivuosi2023

JUFO-taso1


Viimeisin päivitys 2024-15-05 klo 13:01