Zinc Adsorption by Activated Carbon Prepared from Lignocellulosic Waste Biomass (2019)

Tuomikoski, S., Kupila, R., Romar, H., Bergna, D., Kangas, T., Runtti, H., & Lassi, U. (2019). Zinc Adsorption by Activated Carbon Prepared from Lignocellulosic Waste Biomass. Applied Sciences, 9(21), Article 4583. https://doi.org/10.3390/app9214583

JYU-tekijät tai -toimittajat

Julkaisun tiedot

Julkaisun kaikki tekijät tai toimittajat: Tuomikoski, Sari; Kupila, Riikka; Romar, Henrik; Bergna, Davide; Kangas, Teija; Runtti, Hanna; Lassi, Ulla

Lehti tai sarja: Applied Sciences

eISSN: 2076-3417

Julkaisuvuosi: 2019

Volyymi: 9

Lehden numero: 21

Artikkelinumero: 4583

Kustantaja: MDPI AG

Julkaisumaa: Sveitsi

Julkaisun kieli: englanti

DOI: https://doi.org/10.3390/app9214583

Julkaisun avoin saatavuus: Avoimesti saatavilla

Julkaisukanavan avoin saatavuus: Kokonaan avoin julkaisukanava

Julkaisu on rinnakkaistallennettu (JYX): https://jyx.jyu.fi/handle/123456789/67033

Tiivistelmä

Sawdust was used as a precursor for the production of biomass-based activated carbon. Carbonization and activation are single-stage processes, and steam was used as a physical activation agent at 800 °C. The adsorption capacity towards zinc was tested, and the produced activated carbon proved effective and selectively adsorbent. The effects of pH, initial concentration, adsorbent dosage, time, temperature, and regeneration cycles were tested. The adsorption capacity obtained in this study was compared favorably to that of the materials reported in the literature. Several isotherms were applied to describe the experimental results, with the Sips isotherm having the best fit. Kinetic studies showed that the adsorption follows the Elovich kinetic model.

YSO-asiasanat: lignoselluloosa; biomassa (teollisuus); adsorptio; hiili; sinkki (metallit)

Vapaat asiasanat: lignocellulosic biomass; adsorption; carbonization; adsorbent; zinc; regeneration

Liittyvät organisaatiot

Hankkeet, joissa julkaisu on tehty

OKM-raportointi: Kyllä

Raportointivuosi: 2019

JUFO-taso: 1