Effect of Mg2+ ions on competitive metal ions adsorption/desorption on magnesium ferrite : mechanism, reusability and stability studies (2021)


Ivanets, A., Prozorovich, V., Kouznetsova, T., Dontsova, T., Yanushevska, O., Hosseini-Bandegharaei, A., Srivastava, V., & Sillanpää, M. (2021). Effect of Mg2+ ions on competitive metal ions adsorption/desorption on magnesium ferrite : mechanism, reusability and stability studies. Journal of Hazardous Materials, 411, Article 124902. https://doi.org/10.1016/j.jhazmat.2020.124902


JYU-tekijät tai -toimittajat


Julkaisun tiedot

Julkaisun kaikki tekijät tai toimittajatIvanets, Andrei; Prozorovich, Vladimir; Kouznetsova, Tatyana; Dontsova, Tetiana; Yanushevska, Olena; Hosseini-Bandegharaei, Ahmad; Srivastava, Varsha; Sillanpää, Mika

Lehti tai sarjaJournal of Hazardous Materials

ISSN0304-3894

eISSN1873-3336

Julkaisuvuosi2021

Volyymi411

Artikkelinumero124902

KustantajaElsevier

JulkaisumaaAlankomaat

Julkaisun kielienglanti

DOIhttps://doi.org/10.1016/j.jhazmat.2020.124902

Julkaisun avoin saatavuusEi avoin

Julkaisukanavan avoin saatavuus

Julkaisu on rinnakkaistallennettu (JYX)https://jyx.jyu.fi/handle/123456789/73821


Tiivistelmä

The adsorption behavior of magnesium ferrite in single- and multicomponent metal ions solutions in the presence of Mg2+ ions were studied. A dramatic decrease in the adsorption capacity of magnesium ferrite towards Mn2+, Co2+, and Ni2+ ions for comparison study of single- and multicomponent solutions was established. The affinity of the sorbent in accordance with the maximum sorption capacities increases in the following order Cu2+ > Co2+ > Ni2+ > Mn2+. High efficiency of magnesium ferrite regeneration (~100%) with aqueous solutions of magnesium chloride in the concentration range of 0.001-0.1 M was shown. The low degree of toxic metal ions desorption combined with XRD, IR spectroscopy, and EDX analysis data indicate the key role of Mg2+ ion adsorption in the magnesium ferrite adsorbent regeneration. The positive effect of the introduction of Mg2+ ions into multicomponent solutions on metal ions adsorption was established, which is accompanied by an increase in the maximum sorption capacity for all metal ions and especially significant increase in the selectivity towards Cu2+ ions (2.41 mmol/g). The stability of the crystal structure of magnesium ferrite and a low degree of Mg2+ and Fe3+ ions leaching during multiple cycles of adsorption and regeneration of the adsorbent were observed.


YSO-asiasanatkemialliset yhdisteetmagnesiumrautaadsorptioraskasmetallitionit

Vapaat asiasanatmagnesium ferrite; competitive adsorption; mechanism adsorption; regeneration; stability